| Features | high impact resistance, high strength, stress cracking resistance and chemical resistance |
| Application | packaging film, film |
Analysis Item | Quality Index | Test result | Test Method |
| Granular appearance Color grain pcs/kg Large and small grains g/kg | ≤5 ≤10 | 0 0.1 | SH/T 1541-2006 |
Melt mass flow rate g/10min | 6.0～9.0 | 7.6 | GB/T 3682-2000 |
Izod impact strength (23) J/m | ≥25 | 32 | GB/T 1843 |
Tensile yield stress MPa | ≥20.0 | 23.6 | GB/T 1040.2-2006 |
Flexural modulus MPa | ≥650 | 745 | GB/T 9341-2008 |
Fisheye 0.4mm/1520cmü | ≤20 | 6 | GB/T 6595 |
Fisheye 0.8mm/1520cmü | ≤5 | 1 | GB/T 6595 |
 |  |  |  |
 |  |  |
| Features | high impact resistance, high strength, stress cracking resistance and chemical resistance |
| Application | packaging film, film |
Analysis Item | Quality Index | Test result | Test Method |
| Granular appearance Color grain pcs/kg Large and small grains g/kg | ≤5 ≤10 | 0 0.1 | SH/T 1541-2006 |
Melt mass flow rate g/10min | 6.0～9.0 | 7.6 | GB/T 3682-2000 |
Izod impact strength (23) J/m | ≥25 | 32 | GB/T 1843 |
Tensile yield stress MPa | ≥20.0 | 23.6 | GB/T 1040.2-2006 |
Flexural modulus MPa | ≥650 | 745 | GB/T 9341-2008 |
Fisheye 0.4mm/1520cmü | ≤20 | 6 | GB/T 6595 |
Fisheye 0.8mm/1520cmü | ≤5 | 1 | GB/T 6595 |
| | | |
| | |